| 斷裂伸長率 | 480% | 拉伸強度 | 10.6MPa | 密度 | 0.918g/cm3 |
| 熔體流動速率 | 2g/10min | 維卡軟化點 | 98.9℃ | 用途級別 | 流延膜專用料 |
| 規格級別 | 流延膜專用料 | 加工級別 | 擠出級 |
在線訂購支持
在線訂購說明
保障消費者權益，真正做到正品交易，杜絕假冒偽劣產品
021-58958519 13061808058(蔣先生) 13424755533(趙先生)
聯系上海松翰
| 021-58958519 | |
| 13061808058(蔣先生) | |
| 13424755533(趙先生) | |
| |
|
|
產品簡述
詳細數據
訂購指南
| 性能項目 | 試驗條件[狀態] | 測試方法 | 測試數據 | 數據單位 | ||||
| 基本性能 | 比重 | ASTM D-792 | 0.918 | g/cm3 | ||||
| 熔體流動速率 | 190℃/2.16kg | ASTM D-1238 | 2 | g/10min | ||||
| 機械性能 | 電影穿刺能源 | 20.3um | Internal Method | 4.29 | J | |||
| 電影穿刺能源 | 50.8um | Internal Method | 8.81 | J | ||||
| 電影穿刺力 | 20.3um | Internal Method | 44.5 | N | ||||
| 電影穿刺力 | 50.8um | Internal Method | 89 | N | ||||
| 電影穿刺抵抗 | 20.3um | Internal Method | 30.8 | J/cm3 | ||||
| 電影穿刺抵抗 | 50.8um | Internal Method | 24 | J/cm3 | ||||
| 電影韌性 | 20.3um | ASTM D-882 |
|
J/cm3 | ||||
| 電影韌性 | 50.8um | ASTM D-882 |
|
J/cm3 | ||||
| 割線模量-2% Secant | 20.3um | ASTM D-882 |
|
MPa | ||||
| 割線模量-2% Secant | 50.8um | ASTM D-882 |
|
MPa | ||||
| 拉伸屈服強度 | 20.3um | ASTM D-882 |
|
MPa | ||||
| 拉伸屈服強度 | 50.8um | ASTM D-882 |
|
MPa | ||||
| 拉伸斷裂強度 | 20.3um | ASTM D-882 |
|
MPa | ||||
| 拉伸斷裂強度 | 50.8um | ASTM D-882 |
|
MPa | ||||
| 拉伸斷裂伸長率 | 20.3um | ASTM D-882 |
|
% | ||||
| 拉伸斷裂伸長率 | 50.8um | ASTM D-882 |
|
% | ||||
| 落錘沖擊 | 20.3um | ASTM D-1709A | 130 | g | ||||
| 落錘沖擊 | 20.3um | ASTM D-1709B | <100 | g | ||||
| 落錘沖擊 | 50.8um | ASTM D-1709A | 330 | g | ||||
| 落錘沖擊 | 50.8um | ASTM D-1709B | 210 | g | ||||
| 埃爾曼多夫撕裂強度 | 20.3um | ASTM D-1922 |
|
g | ||||
| 埃爾曼多夫撕裂強度 | 50.8um | ASTM D-1922 |
|
g | ||||
| 斷裂拉伸 | 0.0203mm | Internal Method | 300 | % | ||||
| 斷裂拉伸 | 0.0508mm | Internal Method | 470 | % | ||||
| 加工性能 | 熔體溫度 | 274 | ℃ | |||||
| 熱性能 | 維卡軟化點 | ASTM D-1525 | 98.9 | ℃ | ||||
| 熔化溫度 | Internal Method | 123 | ℃ | |||||
| 光學性能 | 光澤度 | 20°，20.3um | ASTM D-2457 | 157 | ||||
| 光澤度 | 20°，50.8um | ASTM D-2457 | 149 | |||||
| 霧度 | 45°，20.3um | ASTM D-2457 | 95 | |||||
| 光澤度 | 45°，50.8um | ASTM D-2457 | 91 | |||||
| 霧度 | 20.3um | ASTM D-1003 | 1 | % | ||||
| 霧度 | 50.8um | ASTM D-1003 | 3 | % | ||||
LLDPE/美國陶氏/HSE-7002 NT 7 包裝圖片
/3.jpg)
/2.jpg)